The Analysis of Current Strength and Electrolysis Process Time of Silver (Ag) Plating on Copper Metal

Sarah Sihotang; Anggita Leontin  Sitorus; Asep Wahyu  Nugraha

doi:10.55927/fjst.v2i6.4419

Authors

Sarah Sihotang FMIPA, Universitas Negeri Medan
Anggita Leontin Sitorus FMIPA, Universitas Negeri Medan
Asep Wahyu Nugraha FMIPA, Universitas Negeri Medan

DOI:

https://doi.org/10.55927/fjst.v2i6.4419

Keywords:

Copper, Electroplating, Ag Metal, Cu Metal, Plating Thickness

Abstract

The purpose of this study was to determine the effect of adding time and increasing electric current strength to the electrolysis process on the quality of Ag metal coating on Cu metal. In this study, the electrolysis process was given different current variations, namely 4A, 6A and 8A and the electrolysis process time was 30, 45 and 60 minutes and the electrolyte concentration remained 0.6 M. To analyze the coating mass and thickness measurements were carried out while to determine the good quality of the coating process was determined using SEM. The results of the study showed that the best coating quality was 60 minutes of coating time and 8A current with a thickness of 4.85 μm. The SEM results to determine the good quality of the coating process on the surface of Ag metal on Cu metal can be seen in the copper sample (concentration 0.6 M, 60 minutes, 8A) which shows that the surface results on copper are slightly better and neater but there are still lots of copper sides which is not silver plated.

Downloads

Download data is not yet available.

References

Adi, F. W. (2018). Studi Eksperimen Finishing Perhiasan Kuningan dengan Perpaduan Elektroplating dan Patinasi. Corak: Jurnal Seni Kriya, 7(1), 54-61.

Bayu, B., Waskito, W., Jasman, J., & Mulianti, M. (2021). kaji eksperimental pelapisan krom menggunakan metode elektroplating. Jurnal Vokasi Mekanika (VoMek), 3(1), 92-98.

Budiyanto, E., Setiawan, D. A., Supriadi, H., & Ridhuan, K. (2017). Pengaruh jarak anoda-katoda pada proses elektroplating tembaga terhadap ketebalan lapisan dan efisiensi katoda baja AISI 1020. Turbo: Jurnal Program Studi Teknik Mesin, 5(1). Elektrokoagulasi Dengan Sel Al-Al. Jurusan Teknik Kimia. Yogyakarta: Universitas Jenderal Achmad Yani.

Ispratiwi, A. W. 2006. Optimasi Waktu Proses Elektrokoagulasi Larutan Yang Mengandung Cu2+, Zn2+dan Cr

Palupi, A. E. (2019). Pengaruh Temperatur Dan Waktu Proses Elektroplating Terhadap Struktur Mikro, Ketebalan Dan Kekerasan Lapisan Nikel Baja St41. Jurnal Teknik Mesin, 7(2).

Rasyad, A., & Budiarto, B. (2019). Analisis Pengaruh Temperatur, Waktu, dan Kuat Arus Proses Elektroplating terhadap Kekuatan Tarik, Kekuatan Tekuk dan Kekerasan pada Baja Karbon Rendah. Jurnal Rekayasa Mesin, 9(3), 173-182.

Riyadi, T. W. B. (2019). Elektroplating Ni/Cu Pada Baja Karbon. Proceeding of The URECOL, 45-50.

S, Sudiglo, R., Suma, H, E., dan Solehudin, A. 2002. Optimasi Kondisi Proses Pada Pelapisan Logam Nikel Dekoratif ( Elektroplating) Untuk Meningkatkan Kualitas Produk Industri Keil Pelapisan Logam, Media Komunikasi Dan Informasi Pengabdian Kepada Masyarakat,. 2 (2) : 1-3.

Sunda, S. S., Wenas, R. S., & Poluan, J. G. (2022). Pengaruh Citra Merek Dan Harga Terhadap Loyalitas Nasabah Produk Logam Mulia Pada Pt. Pegadaian (Persero) Cabang Manado Utara. Jurnal EMBA: Jurnal Riset Ekonomi, Manajemen, Bisnis dan Akuntansi, 10(1), 320-329.

Widayatno, T dan Hamid, 2016. Meningkatkan Efesiensi proses Elektroplating Perak Dekoratif Menuju UMKM Yang Ramah Lingkungan. Simposium Nasional. 10 (5) : 31-36

Yetri, Y., Ultra, M., dan Desmarita, L. 2020. Pengaruh Waktu Temperatur Larutan Terhadap Ketebalan Dan Kekerasan Permukaan Lapisan Hasil Elektroplating Kuningan Pada Baja. Jurnal Teknologi manufaktur. 12 (1) : 55-63