Effect of Alkalized Pineapple Leaf Fiber Direction Variations on Tensile Strength and Bending of Polyester Matrix Composites

Gugun Gundara; Agung Setia Nurzein; Acep Wagiman; Asep Romi Ramadhan

doi:10.55927/fjsr.v2i1.2703

Authors

Gugun Gundara Program Studi Teknik Mesin, Universitas Muhammadiyah Tasikmalaya
Agung Setia Nurzein Program Studi Teknik Mesin, Universitas Muhammadiyah Tasikmalaya
Acep Wagiman Program Studi Teknik Mesin, Universitas Muhammadiyah Tasikmalaya
Asep Romi Ramadhan Program Studi Teknik Mesin, Universitas Muhammadiyah Tasikmalaya

DOI:

https://doi.org/10.55927/fjsr.v2i1.2703

Keywords:

Alkalization (NaOH), Pineapple Leaves, Tensile Test, Bending Test, Fiber

Abstract

Pineapple plant is a plant that is often found throughout Indonesia, so that the production of pineapple is very abundant. Pineapple leaf fiber which consists of about 70-80% cellulose provides high modulus and strength properties, this causes pineapple leaves to be used as an efficient reinforcement of natural fiber composites. In this study, the material used was pineapple leaf fiber which had been alkalized in the direction of 0°, 45°, 90° with a volume fraction of 50% with alkalization (NaOH) treatment for 1 hour and 2 hours, without treatment. This study used polyester resin as the matrix with the hand lay up method. The test results for the pineapple leaf fiber composites which have been alkalized with variations in direction 0°, 45°, 90° with a volume fraction of 50%. And the highest value in the tensile test with treatment is in the 0° direction with a value of 5.883 MPa and an average value of 4.306 MPa with 2 hours of immersion and for the bending test the highest value is in the 0° direction with a value of 3.922 MPa and an average value of 3.276 MPa with 2 hours immersion. The 0° fiber direction has the best stress because the fiber direction is directly proportional to the static load given to the tensile and bending testing machine. Conversely, the direction of 90° is inversely proportional because the direction is not the same as the static load that is given

Downloads

Download data is not yet available.

References

Hadi, T. S., Jokosisworo, S., & Manik, P. (2016). Analisa Teknis Penggunaan Serat Daun Nanas Sebagai Alternatif Bahan Komposit Pembuatan Kulit Kapal Ditinjau Dari Kekuatan Tarik, Bending Dan Impact. Jurnal Teknik Perkapalan, 4(1).

Tauvana, A. I., Syafrizal, S., & Subekti, M. I. (2020). Pengaruh matrik resin-epoxy terhadap kekuatan impak dan sifat fisis komposit serat nanas. Jurnal Polimesin, 18(2), 99-104.

Firman, S. H., Muris, M., & Junaedi, S. (2015). Studi Sifat Mekanik Dan Morfologi Komposit Serat Daun Nanas-Epoxy Ditinjau Dari Fraksi Massa Dengan Orientasi Serat Acak. Jurnal Sains dan Pendidikan Fisika, 11(2), 184-191.

Bahri, F. S., & Aji, A. (2018). Jurnal Teknologi Kimia Unimal. J. Teknol. Kim. Unimal, 2, 85-100.

Sugiyanto, P. (2013). Pengaruh Kekuatan Sambungan Komposit Serat Nanas Terhadap Kekuatan Tarik Dan Geser Dengan Adhesive Epoksi. Jurusan Teknik Mesin–Fakultas Teknik, Universitas Surakarta.

OKTAVILLA, D. D. Y. Pengaruh Alkalisasi Terhadap Kekuatan Tarik Dan Impak Pada Komposit Epoxy Berpenguat Serat Daun Nanas (Doctoral dissertation, FAKULTAS TEKNIK).

Fahmi, H., & Hermansyah, H. (2011). Pengaruh orientasi serat pada komposit resin polyester/serat daun nenas terhadap kekuatan tarik. Jurnal Teknik Mesin, 1(1), 46-52.

Indra, A. T. (2014). Karakterisasi Sistem Sensor Serat Optik Berdasarkan Efek Gelombang Evanescent. Jurnal Fisika Unand, 3(1).

Witono, K., Irawan, Y. S., Soenoko, R., & Suryanto, H. (2013). Pengaruh perlakuan alkali (NaOH) terhadap morfologi dan kekuatan tarik serat mendong. Jurnal Rekayasa Mesin, 4(3), 227-234.

Muhajir, M., Mizar, M. A., & Sudjimat, D. A. (2017). Analisis kekuatan tarik bahan komposit matriks resin berpenguat serat alam dengan berbagai varian tata letak. Jurnal Teknik Mesin, 24(2).

Hidayat, P. (2008). Teknologi pemanfaatan serat daun nanas sebagai alternatif bahan baku tekstil. Teknoin, 13(2).

Zulkifli, Z., & Dharmawan, I. B. (2019). Analisa pengaruh perlakuan alkalisasi dan hydrogen peroksida terhadap kekuatan mekanik komposit serat sabut kelapa bermatriks epoxy. Jurnal Polimesin, 17(1), 41-46.

Fansuri, M. H. (2019). Analisis Uji Tarik Komposit Sandwich Yang Digabungkan Dengan 3D Printing.

Maryanti, B., Sonief, A. A. A., & Wahyudi, S. (2011). Pengaruh alkalisasi komposit serat kelapa-poliester terhadap kekuatan tarik. Jurnal Rekayasa Mesin, 2(2), 123-129.

Fahmi, H., & Hermansyah, H. (2011). Pengaruh orientasi serat pada komposit resin polyester/serat daun nenas terhadap kekuatan tarik. Jurnal Teknik Mesin, 1(1), 46-52.