Analytical Simulation of Biocomposite Materials for Toyota Avanza Vehicle Cabin Lamp Light Covers Utilising Pandanus Tectorius Fibres with Epoxy Matrix as a Manufacturing Substitute to Cut Down on Plastic Waste

Authors

  • Kholis Nur Faizin Politeknik Negeri Madiun
  • Fredy Susanto Politeknik Negeri Madiun
  • M. Shafwallah Al. Aziz Politeknik Negeri Madiun
  • M. Chabib Nur Amin Politeknik Negeri Madiun

DOI:

https://doi.org/10.55927/eajmr.v3i11.11746

Keywords:

Plastic, Biocomposite, Cabin Lamp Cover

Abstract

Biocomposites, made from an epoxy matrix and pandan fibre, offer a biodegradable alternative to plastic. Fabricated through manual layer lay-up, the material underwent stress propagation analysis using SolidWorks simulation and automotive testing. Results indicate that failure occurs in pure tension when stress exceeds 60% of the flexural strength (1.2 MPa) due to longitudinal fibre rupture. With a Young's modulus of 2×10¹⁰ N/m², tensile strength of 13.6 MPa, and Poisson's ratio of 0.31, the material exhibited safe performance under loads nearly four times its capacity. The factor of safety, while as low as 0.5 in critical areas, confirms t

References

Andreas. 2021. Pengaruh Panjang Serat Terhadap Sifat Fisis Dan Mekanik Komposit Serat Pelepah Salak-Epoksi [skripsi]. Medan (ID). Universitas Sumatera Utara.

Dewi 2022. Sherina Muliana. Pengaruh Fraksi Volume Serat Pelepah Daun Pinang Epoksi Terhadap Sifat Komposit [skripsi]. Medan (ID). Universitas Sumatera Utara.

Fajri, R. I. 2013. Studi Sifat Mekanik Komposit Serat Sansevieria Cylindrica Dengan Variasi Fraksi Volume Bermatrik Polyester. Jurnal Fema. 1(2) :85-93.

Gibson, R. F. (1994). Principles Of Composite Material Mechanics. Detroit: McGraw-Hill, Inc.

Ginting, Eva Marlina. 2016. Sifat Mekanis Nano Komposit Termoplastik HDPE Dengan Beberapa bahan Pengisi [skripsi]. Medan (ID): Unimed Press.

Gundara, G., dan Nur Rahman, M. B. (2019). Sifat Tarik, Bending dan Impak Komposit Serat Sabut Kelapa-Polyester dengan Variasi Fraksi Volume.Jurnal Material dan Proses Manufaktur. 3(1): 10-19. 76

Harish Indra Tanarko. (2018). Pengaruh Perlakuan Larutan Koh Terhadap Kekuatan Tarik Komposit Serat Kulit Batang Maja (Aegle Marmelos) Dengan Matriks Epox [skripsi]. Malang (ID). Universitas Brawijaya.

Hasyim, U. H., Yansah, N. A., dan Nuris, M. F. 2018. Modifikasi Sifat Kimia Serbuk Tempurung Kelapa (Stk) Sebagai Matriks Komposit Serat Alam Dengan Perbandingan Alkalisasi NaOH Dan KOH. Seminar Nasional Sains dan Teknologi. Fakultas Teknik Universitas Muhammadiyah Jakarta: 17 Oktober 2018.

Herlinasari, N., dan Suteja, S. 2022. Pineapple Leaf Fiber Reinforced Polyester Composite Modified with Particles from Horse Dung Waste: Characterization of Mechanical Properties and Morphology. Journal of Fibers and Polymer Composites. 1(1): 20–33.

Hoten, H. V. 2020. Analisis Karakterisasi Serbuk Biokeramik Dari Cangkang Telur Ayam Broiler. Jurnal Rotor. 13 (1): 1-5.

Hull, D. dan Clyne, T.W. 1996. An Introduction to Composite Materials.London: Cambridge University Press.

Ibrahim, A. M., Pradana, A. F., Priyosakti, G., dan Arifin, M. 2020. Limbah Industri Gandum Kota Cilegon Sebagai Bahan Baku Sintesis Bioetanol. Jurnal Penelitian Hasil Hutan. 38(2): 91-104

Sari, S. F 2023., Karakterisasi Sifat Mekanik, Kmiawi Dan Morfologi Material Komposit Berpenguat Serat Alam Pandanus Tectorius Berdasarkan Fraksi Volume Serat [Skripsi]. Madiun (ID) Politeknik Negeri Madiun

Downloads

Published

2024-11-28

How to Cite

Faizin, K. N. ., Susanto, F. ., Aziz, M. S. A., & Amin, M. C. N. . (2024). Analytical Simulation of Biocomposite Materials for Toyota Avanza Vehicle Cabin Lamp Light Covers Utilising Pandanus Tectorius Fibres with Epoxy Matrix as a Manufacturing Substitute to Cut Down on Plastic Waste. East Asian Journal of Multidisciplinary Research, 3(11), 5231 –. https://doi.org/10.55927/eajmr.v3i11.11746